| TSR-820 | TSR-821 | TSR-828 | TSR-829 | TSR-755 | TSR-1920 | HS-680 | HS-690 | HS-696 | |||
|---|---|---|---|---|---|---|---|---|---|---|---|
| LASER |  | Ar/LD | Ar/LD | LD | LD | LD | Ar/LD | LD | LD | LD |  |
| Base Resin | | EP | EP | EP | EP | UA | UA | EP | EP | EP | |
| Viscosity(mPa・s)/25℃ | | 300 | 380 | 330 | 210 | 6,000-10,000 | 1,040 | 380-460 | 690 | 360 | |
| Specific Gravity/25℃ | | 1.13 | 1.12 | 1.14 | 1.07 | 1.50 | 1.10 | 1.15 | 1.15 | 1.15 | |
| Ec(mJ/cm^2) | | 20 | 20-25 | 20-24 | 24.6 | 4-5 | 22.6 | - | 8-18 | - | |
| Dp(mm) | | 0.15 | 0.15 | 0.18 | 0.2 | 0.12 | 0.224 | 0.17-0.18 | 0.15-0.17 | 0.18 | |
| E10(mJ/cm^2) | | 120 | 100-120 | 75-85 | 85 | 40 | 70 | 80-90 | 100 | 54 | |
| Tensile Strength(MPa) | | 78 | 49 | 55-60 | 46 | 75 | 3.9 | 80 | 70 | 64 | |
| Elongation(%) | | 6 | 13-15 | 8-10 | 8 | 1-2 | 81 | 3-4 | 8-10 | 6-7 | |
| Tensile Modulus(MPa) | | 2,840 | 1,800 | 2,100-2,200 | 1,750 | - | 10 | 2,380 | 2,000-2,100 | 2,300 | |
| Flexural Strength(MPa) | | 108 | 70 | 80-90 | 68 | 133 | - | 100 | 90 | 84 | |
| Flexural Modulus(MPa) | | 3,060 | 2,225 | 2,500-2,600 | 2,070 | 14,500 | - | 3,200 | 2,200-2,500 | 2,500 | |
| Impact Strength (notched) | | 28-32 | 48-49 | 30-40 | 34 | - | - | 25 | 35-50 | 51 | |
| HDT @ 1.81 MPa | | 62 | 49-52 | 52-53 | 49.4 | 264 | - | 56(100)* | 55-61 | 52-57 | |
| Surface Hardness (Shore D) | | 87 | 82-85 | 84-86 | 83 | 93 | A70 | 85-87 | 82-85 | 83-86 | |
| Appearance | | Transparent | Pale white | Transparent | Highly transparent | Opaque white | Heat-resistant | Pale yellow | Pale yellow | Pale yellow | |
| Feature | | For standard use | Durable model | Durable | Humidity-resistant | Heat-resistant | Rubber model | Highly accurate | ABS | ABS | |
※The data in parentheses () was measured after heat treatment.
※The data is subject to change without notice.
※EP: Epoxy Based, UA: Urethane Acrylate Based
※The data is subject to change without notice.
※EP: Epoxy Based, UA: Urethane Acrylate Based